A dip coating system was projected and constructed to deposit a large range of thin films onto solid substrates. A microcontroller was used to control the deposition system. As an example of application multilayer graphene (MLG) films were deposited onto glass slices in order to obtain conductive films with relatively good light transmittance. The MLG flakes were obtained using natural graphite and isopropyl alcohol resulting in three dispersions treated in ultrasound for 30, 60 and 90 minutes, respectively. Using atomic force microscopy, UV-Vis spectrometry and an electrometer the film characterizations were performed. MLG flakes about 13 nm thick, 10 mµ2 of area were observed using AFM. In films obtained with 35 immersions the electrical resistance and the resistance sheet reached 1.8 kΩ and 1.9kΩ/square respectively. The light transmittance reached 10-20% while films obtained with dispersions treated for 60 and 90 minutes were electrically continuous. Thus, conductive films can be used in chemiresistor sensors, electrochemical and supercapacitors electrodes.

Interactions of cationic dye methylene blue (MB) with clay particles in aqueous suspension have been extensively studied. As already known, the number of natural negative charges on the clay modifies significantly the particle sizes dispersed in water and therefore the nature of the interaction with the dye. This work evaluated with UV-Vis spectroscopy method how the clay particle sizes weighted on the adsorption and rearrangement of the dye molecules in aqueous system. The results obtained from light-scattering measurements confirmed that larger particles are found in suspensions containing the high-charged clays as the visible absorption band related to the MB aggregates (570 nm) on these suspensions prevailed.